Is anybody having the same problem I have with these kodak Isp lens craking when they are being :angry: mounted in the Marchon Airlock or the Sillouhte frames
Is anybody having the same problem I have with these kodak Isp lens craking when they are being :angry: mounted in the Marchon Airlock or the Sillouhte frames
I am not familiar with this material?
Craig
Not sure the material or age of said material you're using, the Rx, final finished thickness and the drill points or any hint of what may or may not have been or is being used to clean the lenses in question. That being said, I have had far more problems with the Marchon Air Lock design, and almost none at all with Silhouettes. So much so that we've dropped the Marchon's from two of my practices outright.
The kodak is a trivex material the problem is the front of the lens is plastic this being the transition part the back is trivex when you edge the lens as a driil job you can see this .The marchon Airlock cracks more than the sillohette but the other problem is even if they make it to the optician some do not know how to adjust a drill mount and they crack that way. Also the stress over time can cause it to crack . This is the problem that I am having I do 60 drill jobs a day I use the CNC optidrill I change my drill bits evey two days .:D
You might want to adjust your Trivex settings in your Optidrill (I use one too). Have it set to take less material than poly each time the bit goes into the lens (I totally forgot what that term is!), that should reduce the amount of stress you're putting on those drill holes. You might want to try different drill bits. We started using one from Optek that has a "fishtail" tip, which keeps the poly and trivex swarf from wrapping itself and melting around the drill bit. It's saved me countless lenses, as well as adjusting the trivex settings.
..
Last edited by Deleted1234; 10-20-2010 at 06:28 PM.
There should be no difference in the cracking of lenses with either mounting system; if you are using Trivex, there is no cracking! We do many drill mounts and the we use as much trivex as possible- phoenix is the real favorite-the rest is poly polarized and 1.67.
With drilling at the proper angles, there should not be a cracking issue.
The drill bit with the "fishtail tip" is the bit of choice. We just started to order them from www.precisebits.com and they are 1/3 the price. i ordered 10 of them for $100 delivered, we were paying almost $40 per bit.
The correct material and bit at the proper base curve = zero breakage.
Hope this helps and i will find out what ISP is.
Craig
think evvile's refering to the imbibed portion of the lens, when he mentioned cr-39?
Neither am I. Google refers you directly to this thread........so that is a dead end................it also refers Isp as internet service provider.
www.signetarmorlite.com makes Kodak lenses, and they do have one in Trivex as per their website.