Does anybody have problems surfacing there mid-index product.
It seems to be a very brittle,we have problems achieving good
thickness with this lens. Any help or is this lens just junk?
Does anybody have problems surfacing there mid-index product.
It seems to be a very brittle,we have problems achieving good
thickness with this lens. Any help or is this lens just junk?
Silicon or aluminum?
Their Sunsensor 1.56 products are very brittle, we stopped doing these in rimless and deblock them in the reclaim tank.Originally Posted by WorldVisionGuy
Rick
We use a wax block system. This has to be one of the worst lens that I have had the
pleasure in using in the 20 years that I have been making glasses. Do you use there
product? If so what thickness do use on the mid-index? Thanks for the suggestions!!!
Scott
We use the Dac 6015n 1st fine
Dac 1300n 2nd fine
Dac 0400 blue polish pad
Once had an issue with SA mid. index, aluminum pads were the culprit.
SA should be able to advise you on this issue.
Post results
James
James if you dont mind me asking, what type pads do you use?
What Pin Pressure do you run on your cylinder machines?
Scott
Haven't had a chance to play in the lab much for quite some time.:shiner: